(a) Optical microscopy image of the Al alloy surface in a sodium chloride solution without pH buffering. Discoloration of intermetallic compounds and the deposition of corrosion products increase over time. (b) Optical microscopy image of the Al alloy surface in a boric-borate buffered sodium chloride solution. Discoloration and corrosion product deposition are suppressed, allowing the pit initiation site to be clearly observed. Credit: Journal of The Electrochemical Society (2026). DOI: 10.1149/1945-7111/ae3647

Researchers at Tohoku University have developed a new technique to identify the initiation sites of a destructive process called pitting corrosion, which occurs when aluminum (Al) alloys are exposed to sodium chloride solutions. This advancement is expected to accelerate the development of Al alloys with improved corrosion resistance. Since Al alloys are widely used in transportation equipment, improving corrosion resistance means we can develop more durable automotive engines, suspensions, and transmissions.

The research was published online in the Journal of The Electrochemical Society on January 20, 2025.

Al alloys are an excellent choice for transportation equipment due to their low weight and recyclability. However, their long-term durability is constantly being challenged by diverse and harsh operating environments. Because Al alloys contain complex microstructures, identifying the origin of corrosion has remained difficult.

"This innovative study combines real-time optical microscopy with a boric–borate buffer solution, in order to suppress discoloration around intermetallic compounds, prevent the deposition of corrosion products, and enable clear visualization of the exact locations where pits form," explains Masashi Nishimoto from Tohoku University.

The research team applied their technique to ADC12 (Al-12%Si-2%Cu), a die-cast Al alloy used for various automotive parts. Since alloys are a mixture of different metals and impurity elements (such as Cu, Fe, Mn, and Mg), numerous intermetallic compounds form during the solidification process, creating electrochemical inhomogeneities that are thought to cause pitting corrosion.

However, conventional corrosion tests in sodium chloride solutions result in widespread discoloration of intermetallic compounds and deposition of corrosion products, obscuring pit initiation sites. This makes it difficult to pinpoint the precise cause.

Cross-sectional scanning transmission electron microscopy image and corresponding energy-dispersive X-ray spectroscopy elemental maps of a pit initiation site identified using the developed technique. Credit: Journal of The Electrochemical Society (2026). DOI: 10.1149/1945-7111/ae3647

By using a boric–borate buffer solution, the newly developed technique suppresses alkalization on intermetallic compounds. This prevents discoloration and reduces corrosion product deposition, allowing clear observation of pit initiation and early growth.

Subsequent analysis by scanning transmission electron microscopy and energy-dispersive X-ray spectroscopy revealed that pits originate in the final solidification region. However, not all final solidification regions become a pit, which suggests that pit initiation also depends on specific local chemical compositions and microstructural features.

"Being able to observe where and how these pits form is an exciting advancement, since it may help us find ways to prevent or slow down their formation for more long-lasting vehicle components," remarks Nishimoto.

The method can be applied beyond die-cast alloys to elucidate pitting corrosion mechanisms in other Al alloys. By clarifying causal relationships between microstructure and corrosion behavior, it contributes to guidelines for designing materials with higher corrosion resistance and supports the development of longer-lasting automotive components.

Publication details

Kaito Takeuchi et al, Identification of Submicron-Sized Sites Causing Localized Corrosion Initiation and Growth in Die-Cast Al–Si–Cu Alloy, Journal of The Electrochemical Society (2026). DOI: 10.1149/1945-7111/ae3647

Citation: Identifying corrosion initiation sites in aluminum alloys (2026, January 21) retrieved 21 January 2026 from https://phys.org/news/2026-01-corrosion-sites-aluminum-alloys.html

This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.